Nano composites of PVDF with ionic liquid [EMIM][TF2N] (IL) modified MWNTs were prepared by melt blending to design materials for EMI shielding applications. MWNTs and IL were mixed in two different ratios (1:1 and 1:5) to facilitate better dispersion of MWNTs in PVDF. It was observed that noncovalent interactions between IL and PVDF resulted in a better dispersion of CNTs and was consistent with increasing concentration of IL. Interestingly, IL modified MWNTs induced the formation of γ-phase crystals in PVDF, which was further confirmed by XRD, FTIR and DSC. Melt rheological measurements and DSC analysis revealed the plasticization effect of IL in PVDF composites further manifesting in a decrease in the storage modulus and the glass transition temperature. This phenomenal effect presumably led to better dispersion of IL modified MWNTs in PVDF further resulting in a significant improvement in electrical conductivity and structural properties. More interestingly, the elongational properties in the composites improved with IL modified MWNTs in striking contrast to MWNT filled PVDF composites. The ac conductivity of the composites reached about 10-3 Scm-1 with the addition of 2 wt% IL modified MWNTs (1:1). This further led to a high electro-magnetic interference (EMI) shielding effectiveness of about 20 dB at 2 wt% IL modified MWNTs. Such materials can further be explored for flexible, lightweight EMI shielding materials for a wide range of operating frequency. © 2014 IOP Publishing Ltd.